High Quality HDPE / LDPE / LLDPE Granules
Specification
Technical Parameter
|
Product name
|
HDPE Granules
|
|
Type
|
Plastic Raw Materials Granules
|
|
Color
|
Transparent and other colors
|
|
Shape
|
Pellet – Granules
|
|
Application
|
Packaging of all kinds of articles
|
|
Density
|
0.924 g/cm3
|
|
MFR
|
0.6 – 0.8 G/10 Min
|
|
Melting point
|
110~115℃
|
|
Processing
|
150~210℃
|
Film grade
|
Item
|
Test condition
|
Test Method
|
Value
|
Unit
|
|
Density
|
ISO 1183
|
0.944-0.955
|
g/cm3
|
|
|
MFR
|
190°C/2.16kg
|
ISO 1133
|
0.03-0.07
|
g/10min
|
|
Tensile strength at yield
|
ISO 527-2
|
22
|
MPa
|
|
|
Elongation at break
|
ISO 527-2
|
>350
|
%
|
|
|
ESCR
|
F50,50°C,100%
|
ASTM D-1693A
|
1000
|
h
|
|
VICAT
|
ASTM D-1525
|
126
|
°C
|
Blow Grade
|
Item
|
Test Condition
|
Test Method
|
Value
|
Unit
|
|
Density
|
ISO 1183
|
0.950~0.955
|
g/cm3
|
|
|
MFR
|
190°C/2.16kg
|
ISO 1133
|
1.7~2.5
|
g/10min
|
|
Tensile strength at yield
|
ISO 527-2
|
24
|
MPa
|
|
|
Elongation at break
|
ISO 527-2
|
>600
|
%
|
Injection Grade
|
Item
|
Test Condition
|
Test Method
|
Value
|
Unit
|
|
MFR
|
190°C/2.16kg
|
ASTM D-1238
|
20
|
g/10min
|
|
Density
|
—
|
ASTM D-792
|
0.954
|
g/cm3
|
|
Tensile strength at yiled
|
—
|
ASTM D-638
|
28
|
MPa
|
|
Elongation at break
|
—
|
ASTM D-638
|
250
|
%
|
|
Impact tensile strength
|
—
|
ASTM D-1822
|
42
|
kJ/m2
|
|
ESCR
|
—
|
ASTM D-1693
|
3
|
—
|
|
VACIT
|
—
|
ASTM D-1525
|
127
|
°C
|
HDPE Cable Grade
|
Property
|
Unit
|
Typical Value
|
|
Mass density
|
g/cm3
|
0.941-0.959
|
|
Melt flow Rate(190 centidegree /2.16kg)
|
g/10min
|
≤1.0
|
|
Tensile yield strength
|
MPa
|
≥19.0
|
|
Flexural modulus
|
Mpa
|
≥965
|
|
Elongation@ break
|
%
|
≥400
|
|
Impact Embrittlement temperature
|
Centidegree
|
MAX -118
|
|
Dielectric Constant
|
100KHZ
1MHZ |
2.32
2.31 |
|
Loss Tangent
|
100KHZ
1MHZ |
MAX 0.0001
MAX 0.0001 |
|
Volume resistivity
|
OHM-CM
|
MIN 1×10 15
|
|
Application
|
Mainly used for the production of high toughness of the telephone,cable insulation material
|
|
High Quality HDPE / LDPE / LLDPE Granules
1. Grade:
1. Blow molding grade,
2. Injection molding grade,
3. Film grade;
4. Extrusion grade.
2. APPLICATION:
Make barrela, plastic bottle and bag, make all kind of pipes, make shading net, and make cable wire-insulating.
3. HDPE granule, Data Sheet
| HDPE cable material
Property |
Unit | Typical Value |
| Mass density | g/cm 3 | 0.941-0.959 |
| Melt flow Rate(190 centidegree /2.16kg) | g/10min | ≤1.0 |
| Tensile yield strength | MPa | ≥19.0 |
| Flexural modulus | Mpa | ≥965 |
| Elongation@ break | % | ≥400 |
| Impact Embrittlement temperature | centidegree | MAX -118 |
| Dielectric Constant | 100KHZ | 2.32 |
| 1MHZ | 2.31 | |
| Loss Tangent | 100KHZ | MAX 0.0001 |
| 1MHZ | MAX 0.0001 | |
| Volume resistivity | OHM-CM | MIN 1×10 15 |
| Application | Mainly used for the production of high toughness of the telephone,cable insulation material | |